Magnetic core loss of ultrahigh strength FeCo alloys
MetadataShow full item record
Hiperco® 50 alloy heat treated between 450 and 650°C exhibits superior mechanical properties. We report the measurements of the ac core loss at various frequencies up to 4500 Hz of the Hiperco® 50 alloy samples annealed at 450 and 650°C. The 650°C annealed specimens have lower ac core loss than that of the 450°C annealed ones. The total core loss, consisting of contributions from hysteresis core loss and eddy-current core loss, depends on frequency f as af+bf2. The eddy-current loss of a single laminate is minor compared to the hysteresis loss.
Showing items related by title, author, creator and subject.
Sun, L.; Zhou, S.M.; Searson, P.C.; Chien, C.-L. (American Institute of Physics, 2003-05-15)Exchange bias in ferromagnetic (FM)/antiferromagnetic (AF) bilayers is usually investigated in the longitudinal configuration with the exchange coupling established in the film plane. In this work, we report on the ...
McQueeney, R.J.; Diallo, S.O.; Antropov, V.P.; Samolyuk, G.D.; Broholm, C.; Ni, N.; Nandi, S.; Yethiraj, M.; Zaretsky, J.L.; Pulikkotil, J.J.; Kreyssig, A.; Lumsden, M.D.; Harmon, B.N.; Canfield, P.C. (American Physical Society, 2008-11-28)Inelastic neutron scattering measurements of the magnetic excitations in CaFe2As2 indicate that the spin wave velocity in the Fe layers is exceptionally large and similar in magnitude to the cuprates. However, the spin ...
Qiu, Yiming; Bao, Wei; Zhao, Y.; Broholm, C.; Stanev, V.; Tesanovic, Z.; Gasparovic, Y.C.; Chang, S.; Hu, Jin; Qian, Bin; Fang, Minghu; Mao, Zhiqiang (American Physical Society, 2009-08-07)Neutron scattering is used to probe magnetic excitations in FeSe0.4Te0.6 (Tc = 14 K). Low energy spin fluctuations are found with a characteristic wave vector (1212L) that corresponds to Fermi surface nesting and differs ...